440A/B/C马氏体不锈钢
440C是马氏体不锈钢的代表钢种，可经热处理而达到高硬度（所有不锈钢、耐热钢中最高）。通常用于制造轴承、刀具，或腐蚀条件下要求高负荷、高耐磨的塑料模具。
美标中440不锈钢有四个牌号。440A、440B、440C的含碳量依次升高；440F（ASTM A582）则在440C的基础上加大S的含量，是一种易切削钢种。国内对应的牌号有9Cr18、9Cr18Mo等。
>> 牌号对照
|
美国 |
ASTM |
440A |
440B |
440C |
440F |
|
UNS |
S44002 |
S44003 |
S44004 |
S44020 |
|
|
日国 |
JIS |
SUS 440A |
SUS 440B |
SUS 440C |
SUS 440F |
|
德国 |
DIN |
1.4109 |
1.4122 |
1.4125 |
— |
|
中国 |
GB |
7Cr17 |
8Cr17 |
11Cr17 9Cr18Mo |
Y11Cr17 |
>> 成分规范
|
牌号 |
440A |
440B |
440C |
440F |
9Cr18 |
9Cr18Mo |
|
C |
0.60 0.75 |
0.75 0.95 |
0.95 1.20 |
0.95 1.20 |
0.90 1.00 |
0.95 1.10 |
|
Si |
≤1.00 |
≤1.00 |
≤1.00 |
≤1.00 |
≤0.80 |
≤0.80 |
|
Mn |
≤1.00 |
≤1.00 |
≤1.00 |
≤1.25 |
≤0.80 |
≤0.80 |
|
P |
≤0.040 |
≤0.040 |
≤0.040 |
≤0.060 |
≤0.040 |
≤0.040 |
|
S |
≤0.030 |
≤0.030 |
≤0.030 |
≥0.150 |
≤0.030 |
≤0.030 |
|
Cr |
16.00 18.00 |
16.00 18.00 |
16.00 18.00 |
16.00 18.00 |
17.00 19.00 |
16.00 18.00 |
|
Mo |
≤0.75 |
≤0.75 |
≤0.75 |
— |
— |
0.40 0.70 |
|
Ni |
(≤0.50) |
(≤0.50) |
(≤0.50) |
(≤0.50) |
(≤0.60) |
(≤0.60) |
|
Cu |
(≤0.50) |
(≤0.50) |
(≤0.50) |
(≤0.60) |
— |
— |
注：括号内数值表示允许加入，并非强制要求。
>> 硬度
|
牌号 |
硬 度 |
|
|
退火态（HB） |
经过热处理（HRC） |
|
|
440A |
≤255 |
≥54 |
|
440B |
≤255 |
≥56 |
|
440C |
≤269 |
≥58 |
|
440F |
≤269 |
≥58 |
> Nimonic80A镍基高温合金 2024-12-17
> GH4145一种耐腐蚀、耐氧化 2024-12-17
> GH4169一种以Fe-Ni-Cr为基沉 2024-12-17
> GH3625合金在使用温度达 2024-12-17
> GH3600（GH600）镍铬基高温 2024-12-17
> GH2132一种以Fe-Ni-Cr为基的 2024-12-17
> GH2901固溶硬化型变形高温 2024-12-17
上一条:H13/M2/D2模具钢用途 下一条:CuCr与CuCrZr铜材的区别! 返回列表